Présentation du produit

High-density polyethylene self adhesive waterproofing membrane is one kind of polymer waterproof rolling material which is specially developed for the underground and tunnel engineering. It adopts the pre-laying construction technology, and can form a strongly reverse bond with the post-pouring concrete structure. In this rolling material, the extruded sheet of modified polyethylene resin is made as the main waterproof material, while the water-soluble isolation material is adopted as the waterproof bonding layer, and then the protective layer of polyethylene membrane is covered to form the polymer waterproof rolling material. After the self-adhesive layer of rolling material is reacted and concreted with the cast-in-situ and liquid concrete pulp, the gapless bond between the waterproof layer and concrete structure is formed to prevent the hidden danger of water breakthrough between the layers, so that the system reliability of waterproof system can be effectively improved.

Caractéristiques du produit

*The pre-laying & reversely bonding technology of product: Cette technologie forme un ensemble solidaire avec le béton de structure et élimine les faiblesses des systèmes d'étanchéité traditionnels enveloppants..

*La feuille haute résistance supporte efficacement les fissures et les perforations sans couche de protection supplémentaire. Le bétonnage peut commencer dès la mise en place des armatures.

*High bonding strength. The product can form a permanent bond with concrete. It has a higher bonding strength and excellent effect of water retention, so that the leakage probability can be effectively reduced.

*Résiste aux dommages dus aux tassements. Les couches d'étanchéité traditionnelles peuvent se déchirer lors d'un tassement des fondations ou de la couche de protection de protection. Cependant, la membrane pré-appliquée et liée en retour adhère à la structure afin d'éviter les dommages dus aux tassements.

*Light material & easy operation. Une épaisseur de 1,2 mm permet d'atteindre un haut niveau d'étanchéité. Le produit convient aux supports simples ou complexes et peut être posé rapidement par deux opérateurs.

*Waterproof for all weather use. The construction can be done in the multiple environments of rainy season, summer and winter etc.

*Shorten the construction period. The requirement for formation level is not high, and the structure layer is less. The construction is quick and convenient. The construction period will be shortened to over 10 days than that of common rolling material.

*La membrane offre une forte résistance au pelage et à la déchirure, une bonne tenue à l'hydrolyse et une excellente souplesse à basse température.

*La pose ne nécessite ni solvant ni combustible ; elle est sûre et respectueUtilisez de l'environnement.

*The water-soluble isolation material is adopted as the waterproof bonding layer. After it is contacted with the wet concrete, the isolation material will be dissolved and disappeared. The self-adhesive layer of rolling material is directly bonded with the concrete. The bonding strength is high and the effect of anti-water breakthrough is good.

Range of Application

Cette membrane convient aux métros, tunnels, réservoirs, canaux, centres d'enfouissement, stations d'épuration, installations métallurgiques et chimiques, ainsi qu'aux radiers et murs enterrés des bâtiments industriels et civils utilisant la technique de pré-application et de liaison inverse.

Normes applicables

The basic performance indexes of physical mechanics for the rolling materials with Class P, Pre-Laid Waterproof Rolls

Properties	TYPICAL VALUES- 1.2mmTHICK MEMBRANE	TYPICAL VALUES 1.2mmTHICK MEMBRANE	TYPICAL VALUES- 1.5mmTHICK MEMBRANE	TYPICAL VALUES- 1.7mmTHICK MEMBRANE	Test Method
Couleur	White/Light Grey	White/Light Grey	White/Light Grey	White/Light Grey	-
Bare HDPE thickness	0.75mm	0.8mm	0.9mm	1.2mm	ASTM D3767
Tensile Strength	21N/mm2	25N/mm2	25N/mm2	25N/mm2	ASTM D412
Elongation	400%	500%	500%	500%	ASTM D412
Low temperature Flexibility	-25°C	-25°C	-25°C	-25°C	ASTM D1970
Peel Adhesive to concrete	≥1000N/M	≥1500N/M	≥1500N/M	≥1500N/M	ASTM D903
Puncture	≥800N	≥1000N	≥1000N	≥1200N	ASTM E154
Resistance to hydrostatic head	>70mtr	>70mtr	>70mtr	>70mtr	ASTM D751-06(2011)
Linear dimensional change	0.1%	0.1%	0.1%	0.1%	ASTM D1204
UV Exposure test (45 days)	No change	No change	No change	No change	ASTM G153

Conditions de stockage

The height of horizontal storage for the rolling material shall not be over five layers, and the rolling material shall be stacked in a single layer when it is vertically storaged.

Avoid the sun, avoid the rain and pay attention to the ventilation. The ambient temperature should not be higher than 45°C, and the relative humidity should not be over 80%.

Stockez séparément les différents types et formats de produits afin d'éviter toute confusion..

Dans des conditions normales, la durée de conservation est d'un an à compter de la fabrication. Après cette date, le produit doit être contrôlé et déclaré conforme avant utilisation.

membranes d'étanchéité

HDPE Autoadhésive Membrane - Type à recouvrement adhésif

Présentation du produit

Caractéristiques du produit

Range of Application

Normes applicables

Conditions de stockage

Parlons de votre projet !

Appelez-nous

Envoyez-nous un e-mail

Liens utiles

CONTACTEZ-NOUS